OLVS188 Acetic High Temperature Resistant Silicone Sealant

Short Description:

HIGH TEMP RESISTANCE SILICONE SEALANT is one component, general purpose acetic silicone sealant, which can chronically resist high temperature up to 343°C. It has excellent waterproof, anti-bacteria abilities and good adhesion with most construction and engine materials.


  • Color: Red
  • Product Detail

    Product Tags

    Characteristics

    1. Acetic cured, RTV, one component;
    2. Easy to use, fast curing;
    3. Excellent resistance with water, weather;
    4. Excellent resistance with huge temperature changing from -20°C to 343°C;
    5. Density: 1.01g/cm³;
    6. Tack-Free Time: 3~6min; Extrusion: 600ml/min.

    Typical Uses

    1. High temperature situations, such as fireplace frames.
    2. Sealant joints between most non-porous materials such as glass, aluminum, metal and metal alloys.
    3. Typical applications including sealing engine parts,gasket,gears and appliances.

    Application

    1. Clean with solvents such as toluene or acetone to keep the substrate surfaces completely clean and dry;
    2. For better appearance cover outside of joint areas with masking taps before application;
    3. Cut nozzle to desired size and extrudes sealant to joint areas;
    4. Tool immediately after sealant application and remove masking tape before sealant skins.

    Limitations

    1. Unsuitable for curtain wall structural adhesive;
    2. Unsuitable for the airproof location, because it is required to absorb moisture in air to cure for the sealant;
    3. Unsuitable for the frosty or moist surface;
    4. Unsuitable for the continually soggy place;
    5. Can’t be used if the temperature is below 4℃ or above 50℃on the surface of the material.

    Shelf life

    12 months if keep sealing, and stored below 27℃in cool, dry place after the date of production.

    Volume: 300ml

    Technical Data Sheet(TDS)

    The following data are only for reference purpose, not intended for use in preparing specification.

    Acetic High Temperature Fast Curing Silicone Sealant

    Performance

    Standard

    Measured Value

    Testing Method

    Test at 50±5% RH and temperature 23±20C:

    Density (g/cm3)

    ±0.1

    1.02

    GB/T13477

    Skin-Free Time (min)

    ≤180

    3~6

    GB/T13477

    Elastic recovery (%)

    ≥80

    90

    GB/T13477

    Extrusion (ml/min)

    ≥80

    600

    GB/T13477

    Tensile Modulus (Mpa)

    230C

    ≤0.4

    0.35

    GB/T13477

    –200C

    /

    /

    Slumpability (mm) vertical

    ≤3

    0

    GB/T 13477

    Slumpability (mm) horizontal

    not change shape

    not change shape

    GB/T 13477

    Curing Speed (mm/d)

    ≥2

    5

    GB/T 13477

    As Cured -After 21 days at 50±5% RH and temperature 23±20C:

    Hardness (Shore A)

    20~60

    35

    GB/T531

    Elongation of Rupture (%)

    /

    /

    /

    Tensile Strength under Standard Conditions (Mpa)

    /

    /

    /

    Movement Capability (%)

    12.5

    12.5

    GB/T13477

    Storage

    12 Months