1. Structural glazing in high risk glass curtain wall;
2. Can joint the surface of glass and metal to form a single assembly, suitable for curtain wall of SSG system design;
3. For the situation of high requirement to adhesive safety and other purpose;
4. Many other purposes.
1. Neutral curing at room temperature, high modulus and high intensity silicone structural sealant;
2. Excellent resistance to weather, and the service life is over 20 years in the condition of general weather;
3. Excellent adhesion to most common building material (not including copper) without priming in general condition;
4. Good compatibility with other neutral silicone sealants.
1. Please follow JGJ102-2003“Technical Code for Glass Curtain Wall Engineering” in strict;
2. The silicone sealant will release volatile compound during curing, it may be bad to heath if you in breathe the volatile compound for a long time. So please ensure adequate ventilation at workplace or curing area;
3. The silicone sealant will not release any harmful substance and
cause any damage to human body after cured;
4. Keep uncured silicone sealant beyond children's reach. If getting into eyes, wash with running water for several minutes, and then consult a doctor.
OLV8800 Super Performance Glazing Sealant |
|||||
Performance | Standard | Measured Value | Testing Method | ||
Test at 50±5% RH and temperature 23±2℃: | |||||
Density (g/cm3) | ±0.1 | 1.37 | GB/T 13477 | ||
Skin-Free Time (min) | ≤180 | 60 | GB/T 13477 | ||
Extrusion (g/5S) | / | 8 | GB/T 13477 | ||
Slumpability (mm) vertical | ≤3 | 0 | GB/T 13477 | ||
Slumpability (mm) horizontal | not change shape | not change shape | GB/T 13477 | ||
Curing Speed (mm/d) | 2 | 3 | / | ||
As Cured -After 21 days at 50±5% RH and temperature 23±2℃: | |||||
Hardness (Shore A) | 20~60 | 40 | GB/T 531 | ||
Tensile Strength under Standard Conditions (Mpa) | / | 1.25 | GB/T 13477 | ||
Elongation of Rupture (%) | / | 200 | GB/T 13477 | ||
Storage | 12 Months |