OLV628 High Grade Weatherproofing Silicone Sealant

Short Description:

OLV628 Project Transparent Silicone Sealant is a one-part, medial modulus, neutral curing , architectural grade silicone sealant designed for multi-purposes weatherproofing application It has excellent primer less adhesion to most construction materials.


  • Color: Clear, White, Black, Grey and Customized Colors
  • Product Detail

    Product Tags

    Main purposes

    1.  Sealing for coated glass, the materials with polycarbonate, large glass;
    2.  Sealing for windows and doors;
    3.  Excellent adhesive to most common building material.

    Characteristics

    1.  One-part; Room temperature; Neutral curing silicone sealant;
    2.  Non-corrosive to marble, coated glass, concrete, metal (not including copper) etc;
    3.  Quickly speed of curing, excellent adhesion, excellent displacement capability;
    4.  Good compatibility with other neutral silicone sealants.

    Application

    1.  Clean with solvents such as toluene or acetone to keep the substrate surfaces completely clean and dry;
    2.  For better appearance cover outside of joint areas with masking taps before application;
    3.  Cut nozzle to desired size and extrudes sealant to joint areas;
    4.  Tool immediately after sealant application and remove masking tape before sealant skins.

    Limitations

    1.  Unsuitable for curtain wall structural adhesive;
    2.  Unsuitable for the airproof location, because it is required to absorb moisture in air to cure for the sealant;
    3.  Unsuitable for the frosty or moist surface;
    4.  Unsuitable for the continually soggy place;
    5.  Can’t be used if the temperature is below 4°C or above 50°C on the surface of the material.

    Shelf life: 12 months if keep sealing, and stored below 270C in cool, dry place after the date of production.
    Volume: 300ml

    Technical Data sheet(TDS)

    The following data are only for reference purpose, not intended for use in preparing specification.

    OLV 628  Neutral Project  Silicone Sealant

    Performance

    Standard

    Measured Value

    Testing Method

    Test at 50±5% RH and temperature 23±2℃:

    Density (g/cm3)

    ±0.1

    1.01

    GB/T 13477

    Tack-Free Time (min)

    ≤180

    5

    GB/T 13477

    Extrusion g/10S

    /

    9

    GB/T 13477

    Tensile Modulus (Mpa)

    23℃

    0.4

    0.6

    GB/T 13477

    –20℃

    or ﹥0.6

    /

    105℃  weight lost , 24hr  %

    /

    7

    Slumpability (mm) vertical

    not change shape

    not change shape

    GB/T 13477

    Slumpability (mm) horizontal

    ≤3

    0

    GB/T 13477

    Curing Speed (mm/d)

    2

    5

    /

    As Cured -After 21 days at 50±5% RH and temperature 23±2℃:

    Hardness (Shore A)

    20~60

    25

    GB/T 531

    Tensile Strength under Standard Conditions (Mpa)

    /

    0.8

    GB/T 13477

    Elongation of Rupture (% )

    /

    250

    GB/T 13477

    Movement Capability (%)

    /

    20

    GB/T 13477