OLV2800 MS Sealant

Short Description:

OLV2800 MS Polymer Sealant is one part, a non-solvent bonding adhesive based on silane-modified polymers. It is a water-absorbing curing product. The cured adhesive has high strength and elasticity and excellent bonding performance to materials such as glass, ceramics, stone, concrete, and wood. It can be used for bonding various materials.


  • Add: NO.1, AREA A, LONGFU INDUSTRY PARK, LONGFU DA DAO, LONGFU TOWN,SIHUI,GUANGDONG, CHINA
  • Tel: 0086-20-38850236
  • Fax: 0086-20-38850478
  • Product Detail

    Product Tags

    Features

    1. After curing completely, it has excellent properties of anti-ultraviolet erosion, resisting climate ageing, waterproof and high and low temperature maintenance;
    2. It has excellent adhesive performance for bonding with construction substrate like cement, concrete and stone, pollution free;
    3. Good flexibility and low module, it has excellent adhesive performance under the condition of displacement for assembly building joints;
    4. Its appearance is available for lacquer and it can solve finishing process problems like decoration mortar on silicone sealant appearance and stone-like coating.

    Application

    1. Caulk and seal for joints of PC prefabricate of building facades;
    2. Waterproof seal for expansion joints and settlement joints of concrete external wall;
    3. Seal for curtain wall joints like building doors and windows, stone, etc;
    4. Leakproof seal for the roof of a building;
    5. Caulk and seal for balcony and interior.

    Regular Colors

    White, Black, Grey

    Packaging

    Paper Cartridge(300ml, 260ml, 230ml)
    Sausage(590ml, 600ml)

    Technology Data

    The following data are only for reference purpose, not intended for use in preparing specification.

    OLV2800 MS Sealant

    Laboratory test temperature: 21 ℃Laboratory test relative humidity: 75%
    Performance Measured Value Testing Method
    Color Black /
    Density (g/cm3) 1.456 GB/T 13477
    Skin-Free Time (min) Before Aging 180 GB/T 13477
    After Aging
    Extrusion (g/5S) Before Aging 11.52 GB/T 13477
    After Aging 1.72
    Consistency Before Aging 7.9 GB/T 13477
    After Aging 7.3
    Curing Speed (mm/d) 3.00mm/1d GB/T 13477
    4.50mm/2d
    5.50mm/3d
    Hardness (Shore A) 7d 24.3 GB/T 531
    Thermal Weight Loss 105℃24hr % 2.09 GB/T 13477
    Elongation of Rupture (% ) 7d 650 GB/T 13477
    The failure area of bonding with glass % 0 GB/T 13477
    The failure area of bonding with aluminum % 0 GB/T 13477
    The failure area of bonding with concrete  % Without primer 0 GB/T 13477
    Primer added 100
    Storage 9 Months