Designed for use in structural adhesive applications such as factory glazing and curtain wall production
1. Structural capability;
2. Excellent adhesion to most surfaces such as coated glass, metals and paints;
3. Excellent weatherability, durability, and a high resistance to ozone, ultra-violet radiation, temperature extremes.
1. Clean with solvents such as toluene or acetone to keep the substrate surfaces completely clean and dry;
2. Filling out the gaps and edges to ensure two-side binding;
3. Cover outside of joint areas with masking taps before application;
4. For better appearance trim the edges before the sealant solidified;
5. Construct in environment with good ventilation;
6. Keep uncured silicone sealant beyond children's reach. If getting into eyes, wash with running water for several minutes, and then consult a doctor.
1. OLV9988 sealant should not be used for curtain wall structural adhesive applications without the prior written approval of Sihui Olivia Chemical Industry Co., Ltd.;
2. OLV9988 should not come in contact, with or be exposed to sealant that liberate acetic acid;
3. This product is neither tested nor represented as suitable for medical or pharmaceutical uses;
4. The product should not touch any non-abrasive surfaces before solidification.
Shelf life: 12 months if keep sealing, and stored below 270C in cool, dry place after the date of production.
Standard: ASTMC 920 GB 16776-2005
Volume: Large package: A-part 200L in iron drum; B-part 20L in plastic drum
OLV 9988 Structural Glazing Silicone Sealant |
|||||
Performance |
Standard |
Measured Value |
Testing Method |
||
Test at 50±5% RH and temperature 23±20C: |
|||||
Density (g/cm3) |
-- |
A:1.39 B: 1.02 |
GB/T 13477 |
||
Tack-Free Time (min) |
≤180 |
50 |
GB/T 13477 |
||
Extrusion (ml/min) |
/ |
/ |
GB/T 13477 |
||
Slumpability (mm) vertical |
≤3 |
0 |
GB/T 13477 |
||
Slumpability (mm) horizontal |
not change shape |
not change shape |
GB/T 13477 |
||
Period of application(min) |
≥20 |
40 |
GB/16776-2005 |
||
As Cured -After 21 days at 50±5% RH and temperature 23±20C: |
|||||
Hardness (Shore A) |
20~60 |
35 |
GB/T 531 |
||
Tensile Strength under Standard Conditions (Mpa) |
≥0.60 |
0.9 |
GB/T 13477 |
||
Elongation at maximum tensile(%) |
≥100 |
265 |
GB/T 13477 |
||
Storage |
12 Months |