O1 Car Windshields Neutral cure silicone sealant

Short Description:

O1 Auto Neutral Silicone sealant is a one-part neutral cure silicone sealant with excellent adhesion for car windshields. It cures on exposure to moisture to form a waterproof and durable silicone rubber. Excellent adhesion to various construction substrates, such as glass, metal, anodized aluminum, galvanized steel, ceramics, concrete, aluminum composite panel and some surface treated materials. It easily extrudes in a wide climatic conditions and cures at ambient temperature by reaction with moisture in the air to form a durable, flexible silicone rubber.

Add: NO.1, AREA A, LONGFU INDUSTRY PARK, LONGFU DA DAO, LONGFU TOWN,SIHUI,GUANGDONG, CHINA

Tel: 0086-20-38850236

Fax: 0086-20-38850478

Send email to us CHAT NOW

Product Detail

Product Tags

Characteristics

1. One part, neutral room temperature cure to form an elastomeric rubber;

2. Excellent unprimed adhesion to a wide range of materials such as metal, plastic, porcelain and glass;

3. Odor or very little.

Application

Application Tips:

1. Residential decoration filling and sealing, such as Kitchen cabinet, countertop, kitchen & bathroom ceilings; window & door frame; frame and floor tile; wall and tile floor, window sill and window countertop
2. Weatherproof waterproof seal for bus stop signs, booths, billboards and guard house
3. Heating, ventilation, air conditioning applications
4. Seals for trucks, trailers and motor homes
5. Many other industrial and architectural applications

Regular Colors

White, Black, Grey

Packaging

300kg/drum, 600ml/pcs, 300ml/pcs.

Technology Data

O1 Auto Neutral Silicone sealant
Performance		Standard	Measured Value	Testing Method
Test at 50±5% RH and temperature 23±2⁰C:
Density (g/cm³)		±0.1	1.52	GB/T 13477
Skin-Free Time (min)		≤180	26	GB/T 13477
Extrusion (ml/min)		≥80	789	GB/T 13477
Tensile Modulus (Mpa)	23⁰C	﹥0.4	0.60	GB/T 13477
Tensile Modulus (Mpa)	–20⁰C	Or ﹥0.6	/	GB/T 13477
Slumpability (mm) vertical		≤3	0	GB/T 13477
Slumpability (mm) horizontal		not change shape	not change shape	GB/T 13477
Curing Speed (mm/d)		2	3.2	/
As Cured -After 21 days at 50±5% RH and temperature 23±2⁰C:
Hardness (Shore A)		20~60	52.6	GB/T 531
Tensile Strength under Standard Conditions (Mpa)		/	0.85	GB/T 13477
Elongation of Rupture (% )		/	370	GB/T 13477
Movement Capability (%)		25	25	GB/T 13477
Storage	12 Months